Siliven New Material Co., Ltd.
Mental matrix composites
Equipped with integrated functions of temperature resistance, structural load-bearing and lightweight, the material has the
characteristics of low density, high tensile strength, high elastic modulus, and high heat resistance. The density of aluminum
matrix composites can reach 3.0g/cm3, which is over 30% lower than titanium alloy materials. The tensile strength is more than
850MPa, and the elastic modulus E is greater than 100GPa.

SN

BXPA1 Aluminum Matrix Composite Material (T5)

1

Physical Properties &

Mechanical Properties

Specific Properties

indicator

Density(g/cm3)

2.85

Young's modulus(GPa)

100

Elongation(%)

2.5-3%

Yield Strength（MPa）

500

Tensile Strength（MPa）

620

2

Forming Process/ Surface Treatment

Surface Treatment

Forming Process

Micro-arc Oxidation

CNC

Anodic Oxidation


Passivation


3

Application Range/ Supply Form

Application Range

Supply Form

Aerospace Structural Components

Rod Material (Diameter Less than 400 mm, Length 200 mm)

Electronic Packaging


Rail Transit


Automotive



BXPA1 Aluminum Matrix Composite Material (T5)
Possessing high specific strength, specific stiffness, and shear strength,
as well as excellent thermal stability, thermal conductivity, anti-adhesion,
wear resistance, and corrosion resistance.
Its performance is as follows:
Our company uses BXPA1 as the raw material, which can be used
in aerospace, electronic packaging, rail transportation, automotive
and other fields to replace some stainless steel, wear-resistant copper alloys, and titanium alloys, thus achieving weight reduction effects.
Currently, our company has developed products such as large nuts,
reducer turbines, gears, and other products.